Defects Involving Inadequate Bonding


Lack of fusion

Involves lack of complete melting and fusion of some portion of the weld metal in a joint. It may occur either between parent metal and weld metal or between two layers of weld metal. This can occur in fusion welding and pressure welding. The following are the reasons for incomplete fusion:

  • Improper manipulation of electrodes
  • Incorrect position of electrodes
  • Low welding current
  • Too rapid arc advance
  • Improper joint fit up
  • Improper edge cleaning of slag after flame cutting
  • Impurities on the face of the joints in the case of pressure welding.

 


If lack of internal fusion is severe it is considered to be a serious defect. Incomplete fusion at the surface is of more serious consequence. As lack of fusion in the form of incomplete penetration of unbevelled or bevelled joints is not always revealed by radiography, ultrasonic examination is recommended as a supplementary test when lack of fusion is suspected.

 Incomplete penetration

This is incomplete penetration of the weld through the thickness of the joint. This usually occurs at the root of the weld or between the deposits made from both sides of a joint. In double welded joints lack of penetration may occur within the wall thickness as a 'buried' defect. Incomplete penetration at the root is more severe. The reasons are:

  • Incorrect joint design.
  • Improper welding parameters, particularly current.
  • Incorrect electrode size.
  • Incorrect polarity where DC is used.

 


Inadequate joint penetration is not tolerated to any extent in objects which are subjected to either tension or bending stresses. It can initiate brittle fracture under either static or dynamic loads. The unfused root causes stress concentration which could lead to failure without deformation and cracks are initiated from the unfused root. Lack of fusion and incomplete penetration are not permitted by pressure vessel code. This type of defects are easily detected by ultrasonic or radiography. In case of thin ferrous welds, magnetic particle examination can be used.


Related Discussions:- Defects involving inadequate bonding

Velocity of belt, velocity of belt: velocity of belt passing over the ...

velocity of belt: velocity of belt passing over the driver pulley will decrease Now with this velocity belt pass over driven pulley, Now Velocity of Driven = Velocity

How can you test hardness of the prepared mould, Q. How can you test hardne...

Q. How can you test hardness of the prepared mould? Hardness test: The hardness of the prepared mould surface is tested to check the ramming density of the sand. The instrume

Material requisition for quotation procedure, The Mechanical Design Enginee...

The Mechanical Design Engineer/Specialist shall be responsible for mechanical design calculations that are required to ensure that the end product complies with all applicable code

Explain the heterogeneous system - thermodynamic, Explain the Heterogeneous...

Explain the Heterogeneous System - Thermodynamic Heterogeneous System: A system, which involves two or more phase, is known as heterogeneous system. Such as, Water plus steam,

Working of telescopic hydraulic fork , Working of Telescopic Hydraulic Fork...

Working of Telescopic Hydraulic Fork:   When a road shock exerts on to the suspension system it is transmitted to the spring instead of motorcycle frame and the spring starts to o

Determine the stress in steel rod, A steel rod of 3 cm diameters and 5 m lo...

A steel rod of 3 cm diameters and 5 m long is connected to two grips and the rod is maintained pull exerted when the temperature falls to 30 o C if (a) The ends do not yield, an

Vicker''s hardness test, V icke r ' s Hardness Test: This test is ...

V icke r ' s Hardness Test: This test is alike the Brinell test but uses different indenter. A square based pyramid of cone angle 136 ° is used. The applied load can be 5,

Find the maximum torque - i-section, Find the maximum torque - I-section: ...

Find the maximum torque - I-section: An I-section 150 × 80 mm has flanges 6 mm thick and web 4 mm thick. Discover the maximum torque that may be safely applied if the shear st

Determine the origin of step, Determine the Origin of STEP Considerable...

Determine the Origin of STEP Considerable progress has been made in vector data exchange over the recent past. Initially, some CAD/CAM vendors offered direct translator softwar

Write Your Message!

Captcha
Free Assignment Quote

Assured A++ Grade

Get guaranteed satisfaction & time on delivery in every assignment order you paid with us! We ensure premium quality solution document along with free turntin report!

All rights reserved! Copyrights ©2019-2020 ExpertsMind IT Educational Pvt Ltd