A tensile test was conducted on a mild steel bar. The following data was obtain from the testi. Dia of the steel bar= 3 cmii. Gauge length of the bar = 20cmiii. Load at elastic limit=250kNiiii. Extension at a load of 150 kN= .21mmv. Minimum load =380kNvi. Total extension=30 mmvii. Dia of the rod at the failure =2.25cm. Determine:
(a) the young's modulus
(b) the stress at elastic limit
(c) the % elongation
(d) the % decrease in the area
a point charge causes an electric flux of -750 nmc to pass through a spherical gaussian surface of 10.0 cm radius
the operation of a sewing machine requires the 200-mm-long bar to oscillate back-and-forth through an angle of 60
a special c-clamp uses a 0.5-in. diameter acme thread and a collar of 0.625-in. effective mean diameter. the collar is
If it is known that the value of the stress exponent n for this alloy is 8.2, compute the steady-state creep rate at 1300 K and a stress level of 89 MPa.
Consider a Refrigerant 22 at 0oC that is going through a phase change from the saturated liquid to saturated vapor. Using T-dS equations, calculate the entropy change between these two phases.
Two-tenths of a pound of air at 2 atm and 540 degrees R is trapped within a syringe by a plunger at one end and a stopcock at the other, a shown in Fig. P4.103. The stopcock is opened and the plunger moved to inject the trapped air into a container t..
glycerin at 40 degree c with a rho 1252 kgm3 and mu 0.27 kgm s is flowing through a 2cm diameter 25m long pipe that
The yield strength for an alloy that has an average grain diameter of 4.4 x 10-2 mm is 115 MPa. At a grain diameter of 7.1 x 10-3 mm, the yield strength increases to 258 MPa. At what grain diameter, in mm, will the yield strength be 237 MPa?
consider a plate with uniform heat generation q. for k200 wmk q40 mwm3. t1160 c at x0 t2100 c at x2l and a plate
0.78 kg of helium fills a piston-cylinder device (initial volume of 0.5 m3 which is maintained at an absolute pressure of 240 kPa. Heat is added until the volume doubles. What is the temperature of the helium at the end of the process?
A tensile test is performed on a brass specimen 10 mm in diameter using a gauge length of 50 mm. What is the modulus of elasticity E of the brass
getting heat from a hot source that is 100 kpa steam going from saturated vapor to a saturated liquid 1mw of power is
Get guaranteed satisfaction & time on delivery in every assignment order you paid with us! We ensure premium quality solution document along with free turntin report!
whatsapp: +1-415-670-9521
Phone: +1-415-670-9521
Email: [email protected]
All rights reserved! Copyrights ©2019-2020 ExpertsMind IT Educational Pvt Ltd