Cast iron, Mechanical Engineering

CAST IRON:

Cast iron is an important alloy of Fe and C are mostly employed within industry for its convenience to casting in intricate and superior mechanical properties. Steels could also be cast but process is frequently costlier. Figure of Iron-Carbon Phase Diagram, clearly shows the region of cast iron in equilibrium diagram. The demonstration presents that there is a eutectoid at 4.3% as point C such has solidification temperature of 1135oC. Alloys inside carbon range of 2.3% to 4.2% are occasionally submitted to as hypo-eutectic irons, because their carbon content is underneath the eutectic composition. Even though, the melting points of cast irons are higher than various non-ferrous alloys, still they are inside the reach of easy melting furnaces, some of which are commercially accessible. It is one cause as to why cast irons are as popular as structural material.

To know different phases that are represent in a cast iron one may refers as cooling of a typical Fe - C mixture from melt, say one having y % C as in figure of Iron-Carbon Phase Diagram. The first material to solidify is austenite that is an explanation of carbon into fcc iron. The line PG will give the amount of C in solution in austenite during solidification. This amount is all time less than the average percentage in the melt that means carbon is refused out of austenite whilst the liquid phase is enriched in carbon. The last liquid to solidify has the eutectic composition that is 4.3%. The eutectic has the austenite and carbon.

If the liquid is cooled gradually keeping near equilibrium situation, the carbon solidified like flakes of graphite in a soft ferrite matrix, in pearlite or in a mixture of pearlite and ferrite. If liquid is cooled quickly then ferrite is suppressed and cementite and pearlite precipitate.

Casting is a process whether molten is poured in a mould and on solidifying the casting of the shape of mould is acquired. Cast iron, as previously stated, in a superior material for casting. Universal properties of cast iron are as:

a) Cheap material.

b) Lower melting point as 1200oC as compared to steel as 1380-1500oC.

c) Good casting properties foe instant: high fluidity, sound casting, low shrinkage, ease of production in huge number.

d) Good in compression but CI along with ductility are available also.

e) CI is machinable is main cases.

f)  Abrasion resistance is remarkably high.

g) Very significant property of CI is its damping characteristics that isolates vibration and makes it excellent material for foundation and housing.

h) Alloy CI might be good against corrosion.

Posted Date: 2/26/2013 6:47:39 AM | Location : United States







Related Discussions:- Cast iron, Assignment Help, Ask Question on Cast iron, Get Answer, Expert's Help, Cast iron Discussions

Write discussion on Cast iron
Your posts are moderated
Related Questions
Larson-Miller parameter: For material of example of calculate life in hours at temperature of 900oC, and at σ = 20 MPa. Solution Larson-Miller parameter is given by

explain capacity planning system

Function Phase: Steps: 1. To identify the functions. To identify the functions regarding to the problem in radial drilling machine. Our project focus on the create an a

Relationships among VM, Virtual Prototyping, the Virtual Enterprise Virtual Manufacturing (VM) VM is a synthetic, integrated manufacturing environment exercised to improve

Magnitude of the resultant couple: For non-parallel forces also the location of the line of action of resultant may be determined by utilizing R × d = ∑ M o . The magnitu

Gibson Ltd operates sportswear stores in Dublin and Cork and has set the following quarterly sales target for international and provlncial rugby shirts for 2013 per the attached sc

CAST IRON: Cast iron is an important alloy of Fe and C are mostly employed within industry for its convenience to casting in intricate and superior mechanical properties. Stee

Mr. Moody has decided to invest at most N$100 000 in securities in the form of corporate stocks. He has classified his options into three groups of stocks: blue-chip stocks that he

What are the problem arise in pile foundation Problems can also arise in providing pile foundations in residual soils which are underlain by sloping rock. Special rock sockets

Find speed for two hours with HSS tools Find speed for two hours tool life for dry machining of free cutting mild steel with HSS tool. Solution From Table 3, a value o